TURCO PRETREAT W是一種黃色液體化合物，主要用來抑制在非惰性氣體爐中鐵合金，不銹鋼，鎳鉻合金和銅合金的熱處理相關的頑固結垢的形成。在對熱處理合金進行除垢的極其腐蝕性的酸性混合物，如果用Turco Pretreat量是最少的，它也可以減少晶間氧化，抑制粘附氧化物膜的形成。
TURCO PRETREAT W is a yellow liquid compound formulated to inhibit the formation of tenacious scale associated with heat treating of ferrous alloys, stainless steels, nickel chrome alloys and copper alloys in non-inert gas atmosphere furnaces. It also minimizes the need for the extremely corrosive acidic mixtures commonly used to descale heat-treatable alloys. It reduces intergranular oxidation and inhibits the formation of adherent oxide films.
FEATURES:
TURCO PRETREAT W offers these features:
Shortens descaling time, due to ease of oxide removal
Very low metal loss (approx. 0.0002 inches per side)
Minimum equipment requirements
Minimum intergranular attack or surface etching
USE INSTRUCTIONS:
Proper precleaning is essential. Many soils, if not completely cleaned from the metal surface prior to heat treatment, can have very deleterious effects on metal alloys during the heat treat process. Undesirable alloying on the metal surfaces, often accompanied by pitting and other serious defects, can result from failure to preclean in accordance with recommended procedures. Cleaning may be accomplished with TURCO HTC, TURCO VITRO-KLENE, or other suitable TURCO cleaners. Consult the TDB for the cleaner chosen for recommendations on operating parameters.
Thoroughly rinse with overflowing water (warm preferred).
Acid clean in appropriate descaling solution for 5 to 10 minutes (See TDB #496 for recommended procedures). Acid cleaning is not necessary for all conditions, but it is essential where die contaminants such as lead and zinc, not removable in alkaline precleaning, are known or suspected to be present.
Rinse with overflowing water for 2 to 3 minutes.
Allow parts to dry.
APPLICATION OF TURCO PRETREAT W:
After thorough cleaning and drying, apply TURCO PRETREAT W compound as soon as possible to prevent recontamination of metal surfaces.
TURCO PRETREAT W must be thoroughly mixed before using. The best method for application of PRETREAT W is by spray. No thinning is required. Normal suction aspirated spray equipment such as Binks Model 18 is satisfactory for application of the thin film necessary for protection.
* Start with 8 psi Pot Pressure and increase gradually if more material is required for faster application.
Coating thickness must not exceed 0.2 to 0.3 mils. at any location on the part. Thicker coatings will not function properly and can lead to part damage. Special caution must be taken in applying TURCO PRETREAT W to corners or other irregular surfaces. Normally, application of thin box coatings until a uniform light orange-gold coating color appears on the surface is sufficient to obtain the recommended thickness.